HONES® PBT GF10
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Guangdong Shunde Hones Polymer Material Co., Ltd. |
| Trademark: | HONES® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EMIs0Z_HONES-PBT-GF10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Technology characteristics: 10% Glass fiber reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.60 to 1.1 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.090 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 76.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 4000 | MPa | ASTM D790 |
| Flexural Strength | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 30 | kJ/m² | ISO 179 |
| Unnotched Izod Impact (3.20 mm) | 40 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 185 | °C | ASTM D648 |
| CLTE - Flow (-30 to 30°C) | 4.1E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.20 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | V-0 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEETEC LLDPE UF315 | Lotte Chemical Corporation | LLDPE | SEETEC LLDPE |
| SLOVAMID® 6 GF 35 TS | Plastcom | Nylon 6 | SLOVAMID® 6 |
| XAREC™ SP140 | Idemitsu Kosan Co., Ltd. | SPS | XAREC™ |
| Elastollan® L 785 A | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| Osterlene® LDC1821SA | Osterman & Company | LDPE | Osterlene® |