OnForce™ LFT LF5200-5007 BLACK UV
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | OnForce™ LFT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EKuGlW_OnForce-LFT-LF5200-5007-BLACK-UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyvan's long fiber thermoplastic polymers are used in situations where high hardness and good impact resistance are required, such as metal substitution or other structural applications. These products exhibit enhanced physical and mechanical properties compared to staple fiber products. Its advantages include improved impact strength, elasticity and material strength in different temperature ranges. In addition, compared with traditional high-filled short fiber products, long fiber thermoplastic polymers show improved properties in terms of creep and fatigue resistance, improved dimensional stability and unique surface finish. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.34 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11400 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 120 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.5 | % | ISO 527-2 |
| Flexural Modulus | 9600 | MPa | ISO 178 |
| Flexural Stress | 190 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 19 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 52 | kJ/m² | ISO 179 |
| Notched Izod Impact | 18 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, not annealed | 154 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 139 | °C | ISO 75-2/C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 210 - 230 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 5.00 | MPa |
| Injection instructions |
|---|
| LFT compounds can be processed using equipments similar to those used for short fiber products. The mechanical properties depend greatly on the length of the fibers in the moulded part; therefore processing conditions must be set carefully in order to minimize fiber breakage. A "low shear process" is advised, with low back pressure, low screw speed and low to medium injection speed. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIGITRON 30530 GF | Ovation Polymers Inc. | Polyester, TP | RIGITRON |
| Quantum Composites QC-8816 | Quantum Composites Inc. | Vinyl Ester | Quantum Composites |
| SARANEX™ 451 | The Dow Chemical Company | PVDC | SARANEX™ |
| NOVAPOL® LF-Y320 Series | NOVA Chemicals | LDPE | NOVAPOL® |
| Formolene® 4100P | Formosa Plastics Corporation, U.S.A. | PP Homopolymer | Formolene® |