Latene® 7H2W TR/40
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EHdcDT_Latene-7H2W-TR-40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polypropylene homopolymer (PPh). Heat and metal stabilised. Mineral filler. Product UL certified. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.85 to 1.1 | % | |
| Flow : 2.00 mm | 0.90 to 1.1 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 4200 | MPa | |
| 60°C | 1900 | MPa | |
| 90°C | 1000 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 25.0 | MPa | |
| Yield, 60°C | 10.0 | MPa | |
| Yield, 90°C | 8.00 | MPa | |
| Break, 23°C | 25.0 | MPa | |
| Break, 60°C | 13.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 2.5 | % | |
| Yield, 60°C | 3.4 | % | |
| Yield, 90°C | 4.6 | % | |
| Break, 23°C | 3.0 | % | |
| Break, 60°C | 35 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 20 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 30 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 135 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 75.0 | °C | |
| Vicat Softening Temperature | 100 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 6.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 200 to 240 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2800B-70A FR | RTP Company | TPV | RTP |
| Sindustris POM FW716CS | Sincerity Australia Pty Ltd. | Acetal (POM) Homopolymer | Sindustris POM |
| MTEGRITY™ PP Impact Copolymer CP402 | M. Holland Company | PP Impact Copolymer | MTEGRITY™ PP Impact Copolymer |
| Pearlbond™ 508 | Lubrizol Advanced Materials, Inc. | TPU-Capro | Pearlbond™ |
| Petrotene® PP A2 G20 T10 PRTA011 PH204 MSP | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |