LNP™ LUBRICOMP™ QFP36 compound
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EF5voY_LNPLUBRICOMPQFP36compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP QFP36 is a compound based on PA6.10 resin containg Glass Fiber, PTFE, Silicone. Added features include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound QFL-4536 Product reorder name: QFP36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8100 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 118 | MPa | ISO 527-2/5 |
| Tensile Strain (Yield) | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 6200 | MPa | ISO 178 |
| Flexural Stress | 165 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(23°C) | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 55 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 64.0 mm Span) | 198 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 2.3E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.750 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 - 0.20 | % | |
| Rear Temperature | 249 - 260 | °C | |
| Middle Temperature | 260 - 271 | °C | |
| Front Temperature | 271 - 282 | °C | |
| Processing (Melt) Temp | 271 - 277 | °C | |
| Mold Temperature | 82.2 - 93.3 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP PP UP4I203 - Natural | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| Fainplast PVC PH 70/AT | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| ExxonMobil™ HDPE HD 6719 Series | ExxonMobil Chemical | HDPE, UHMW | ExxonMobil™ HDPE |
| Lucent PP GPP-210 | Lucent Polymers, Inc. | PP, Unspecified | Lucent PP |
| Vipel® F085-CAA-00 | AOC, L.L.C. | Vinyl Ester | Vipel® |