Visico ME4425 / Ambicat LE4472 is a silane crosslinkable black compound designed for covering/insulation of overhead cables. The base material Visico ME4425 in combination with the catalyst masterbatch Ambicat LE4472 will accelerate the moisture-induced crosslinking reaction. The system is highly active and crosslinks quickly at ambient conditions, in sauna or in hot water. When properly mixed, addition of 7 parts of Ambicat LE4472 to 93 parts of Visico ME4425 , insulation with excellent thermo-oxidative stability, also in contact with copper as will as aluminium, is achieved. The final product will contain nominal 2,5% of fine size carbon black ensuring excellent weatherability. Visico ME4425 / Ambicat LE4472 contains antioxidant, metal deactivator and a drying agent. Visico ME4425 contains a permanent scorch retardant additive, ensuring safe processing and enabling the use of highly active crosslinking catalyst. Visico ME4425 / Ambicat LE4472 in combination meets the applicable requirements as below when processed using sound extrusion and testing procedure: ANSI/ICEA S-70-547 ASTM D 1248 Type II, Class C, Category 4 HD 626 S1 (TIX-2, TIX-4, TIX-6, TIX-9) HD 603 S1 NEMA WC 70 NEMA WC 71 IEC 60502-1 The standards referred to above is a selection and is not complete coverage of all applicable standards.Contact your Borealis representative for additional information.

Message

Visico ME4425 / Ambicat LE4472 is a silane crosslinkable black compound designed for covering/insulation of overhead cables.

The base material Visico ME4425 in combination with the catalyst masterbatch Ambicat LE4472 will accelerate the moisture-induced crosslinking reaction. The system is highly active and crosslinks quickly at ambient conditions, in sauna or in hot water.

When properly mixed, addition of 7 parts of Ambicat LE4472 to 93 parts of Visico ME4425 , insulation with excellent thermo-oxidative stability, also in contact with copper as will as aluminium, is achieved. The final product will contain nominal 2,5% of fine size carbon black ensuring excellent weatherability.

Visico ME4425 / Ambicat LE4472 contains antioxidant, metal deactivator and a drying agent. Visico ME4425 contains a permanent scorch retardant additive, ensuring safe processing and enabling the use of highly active crosslinking catalyst.

Visico ME4425 / Ambicat LE4472 in combination meets the applicable requirements as below when processed using sound extrusion and testing procedure:

ANSI/ICEA S-70-547

ASTM D 1248 Type II, Class C, Category 4

HD 626 S1 (TIX-2, TIX-4, TIX-6, TIX-9)

HD 603 S1

NEMA WC 70

NEMA WC 71

IEC 60502-1

The standards referred to above is a selection and is not complete coverage of all applicable standards.Contact your Borealis representative for additional information.

General Information
Additive	Antioxidant Carbon Black (3%) Metal Deactivator Scorch Resistant
Features	Antioxidant Crosslinkable Fast Cure Good Processability Good Stability Good Surface Finish Good Thermal Stability Good Weather Resistance Low Die Swell Oxidation Resistant
Uses	Cable Jacketing Insulation
Agency Ratings	ANSI/ICEA S-70-547 ASTM D 1248, I, Class A, Cat. 4 HD 603 S1 IEC 60502-1 NEMA WC-70 , WC-71
Appearance	Black
Forms	Pellets
Processing Method	Extrusion

Physical	Nominal Value	Unit	Test Method
Density ¹	0.940	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	1.0	g/10 min	ISO 1133
Environmental Stress-Cracking Resistance (50°C, 10% Igepal, F20)	> 96.0	hr	IEC 60811-4-1/B

Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore D, 1 sec)	55		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Yield)	> 20.0	MPa	ISO 527-2/250
Tensile Strain (Break)	> 300	%	ISO 527-2/250

Aging	Nominal Value	Unit	Test Method
Change in Tensile Stress (135°C, 240 hr)	< 25	%	IEC 60811-1-2

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature	< -76.0	°C	ASTM D746
Hot Set			IEC 60811-2-1
200°C ²	60	%
200°C ³	0.0	%

Additional Information	Nominal Value	Unit
Crosslinking
23°C, 700.0 µm ⁴	1.5	day
23°C, 1.80 mm ⁵	7.0	day
90°C, 700.0 µm ⁶	< 15.0	min
90°C, 1.80 mm ⁷	1.00	hr

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	> 1.0E+16	ohms·cm	IEC 60093
Electric Strength	> 20	kV/mm	IEC 60243-1
Dielectric Constant (50 Hz)	< 2.50		IEC 60250
Dissipation Factor (50 Hz)	< 6.0E-4		IEC 60250

Extrusion	Nominal Value	Unit
Cylinder Zone 1 Temp.	150	°C
Cylinder Zone 2 Temp.	185	°C
Cylinder Zone 3 Temp.	185	°C
Cylinder Zone 4 Temp.	185	°C
Melt Temperature	190 to 195	°C
Die Temperature	185	°C

Note Message
1 .	Mixture 95:5, ISO 1872-2
2 .	Elongation under load, 0.20 MPa
3 .	Permanent deformation, 0.20 MPa
4 .	In air, 50 % humidity
5 .	In air, 50 % humidity
6 .	Sauna or water bath
7 .	Sauna or water bath

Resin Grade	Manufacturer	Category	Trademark
Ravamid® B ST BK45	Ravago Group	Nylon 6	Ravamid®
Starex SR-0320	SAMSUNG SDI CO., LTD.	ABS	Starex
Wanthane® WHT-8280H	Wanhua Chemical Group Co., Ltd.	TPU-Polyether	Wanthane®
Latistat 47/7-03	LATI S.p.A.	PP Copolymer	Latistat
SABIC® PPcompound 7705	Saudi Basic Industries Corporation (SABIC)	PP, Unspecified	SABIC® PPcompound

Resin Grade

Manufacturer