ESENTTIA 12R88A
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Polipropileno del Caribe S.A. |
| Trademark: | ESENTTIA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EBSNLN_ESENTTIA-12R88A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Characteristics: Control reologhy Random copolymer polypropylene; good impact resistance; with antistatic additive. Recommended for: General purpose injection molding applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) 1(230°C/2.16 kg) | 13 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield, 3.20 mm, Injection Molded) | 25.5 | MPa | ASTM D638 |
| Tensile Elongation 3(Yield, 3.20 mm, Injection Molded) | 13 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 4(3.20 mm, Injection Molded) | 896 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 53 | J/m | ASTM D256A |
| Gardner Impact 5(23°C, 3.20 mm, Injection Molded) | 26.6 | J | ASTM D5420 |
| Note Message | |
|---|---|
| 1 . | Procedure B |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 1.3 mm/min |
| 5 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumitomo PP AZ764 | Sumitomo Chemical Asia | PP Copolymer | Sumitomo PP |
| YUNGSOX® PP 5060 | Formosa Polypropylene | PP Random Copolymer | YUNGSOX® PP |
| Bluestar Epoxy WSR6101 | Bluestar New Chemical Materials Co. Ltd | Epoxy | Bluestar Epoxy |
| PLUSTEK PB508 | Polyram Ram-On Industries | Nylon 6 | PLUSTEK |
| Sylvin 6407-83 Black | Sylvin Technologies Incorporated | CPE | Sylvin |