NEONIT® K82 L8
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | SBHPP |
| Trademark: | NEONIT® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EB6W43_NEONITK82L8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NEONIT® K82 L8 is a long glass fiber reinforced high temp. epoxy molding compound for applications demanding heat resist., high mech. properties & long term dim. stability at high temp. (as jet engines or indus. equipment), recommended for parts with metal inserts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.80 | g/cm³ | ISO 1183 |
| Apparent Density | 0.50 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.10 - 0.30 | % | ISO 2577 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 140 | MPa | ISO 527-2 |
| Tensile Strain (Break) | < 1.0 | % | ISO 527-2 |
| Flexural Modulus | 20000 | MPa | ISO 178 |
| Flexural Stress | 260 | MPa | ISO 178 |
| Compressive Stress | 200 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 80 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, not annealed | > 250 | °C | ISO 75-2/Af |
| 8.0 MPa, not annealed | > 200 | °C | ISO 75-2/C |
| Glass Transition Temperature | > 220 | °C | TMA |
| Thermal Conductivity | 0.40 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 5.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 180 | kV/mm | IEC 60243-1 |
| Relative Permittivity (23°C, 1 MHz) | 6.00 | IEC 60250 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Delrin® 327UVE RD402 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| EPLAMID 6 CFR 10 NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 6 | EPLAMID 6 |
| Karina WHITE COLOR CONCENTRATE MBU 10/0085-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 50/CF/10/GF/10/TF/10/BK | Lehmann & Voss & Co. | PC | LUVOCOM® |
| Pacrel® 5365N-AC | Nanjing Jinling OPTA Polymer Co., Ltd. | TPE | Pacrel® |