| DESCRIPTION: Epocast® 1617-A/B epoxy syntactic is a low-density, self-extinguishing compound for edge sealing honeycomb structures. The lightweight epoxy is an easy-to-handle material that exhibits high strength after curing. Epocast® 1617-A/B epoxy syntactic cures to an off-white color and is qualified to BMS 5-28, Type 17. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D1622 | ||
| -- 1 | 0.650 | g/cm³ | ASTM D1622 |
| -- 2 | 0.700 | g/cm³ | ASTM D1622 |
| -- 3 | 1.05 | g/cm³ | ASTM D1622 |
| Viscosity | ASTM D2196 | ||
| -- 4 | Paste | ASTM D2196 | |
| -- 5 | Paste | ASTM D2196 |
| Flammability | Nominal Value | ||
|---|---|---|---|
| Flammability | Self-extinguishing |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time - 50 gms (25°C) | 1.0 - 1.5 | hr | ASTM D2471 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cure Time (25°C) | 7.0 | day | |
| Tensile Lap Shear - AL/AL (25°C) | 6.89 | MPa | ASTM D1002 |
| Weight Gain 6 | ASTM D543 | ||
| Distilled water : 25°C | % | ASTM D543 | |
| Mil-M-5606, hydraulic fluid : 25°C | % | ASTM D543 | |
| Mil-S-3136, Type III test fluid : 25°C | % | ASTM D543 | |
| Skydrol 500-A : 25°C | % | ASTM D543 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Modulus | 1720 | MPa | ASTM D695 |
| Compressive Strength (25°C) | 37.9 | MPa | ASTM D695 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Resin | Mixing ratio by weight: 100 | ||
| Hardening method | Mixing ratio by weight: 20 | ||
| Thermoset Mix Viscosity 7 | 50000 | cP | ASTM D2196 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CURE SCHEDULE: 7 days at 77°F (25°C) or gel at room temperature plus five hours at 125°F (52°C). |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | System |
| 3 . | Hardener |
| 4 . | System |
| 5 . | Resin |
| 6 . | on immersion - 24 hrs |
| 7 . | Hardener |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Di-Pak™ R-4528/30 | Hapco Inc. | TP, Unspecified | Di-Pak™ |
| Ferro PP TPP20AA11BK | Ferro Corporation | PP Homopolymer | Ferro PP |
| EPO-TEK® E2036 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| POLYCASA® ACRYL G 66 | Polycasa | Acrylic (PMMA) | POLYCASA® ACRYL |
| Adsyl 7624 XCP | LyondellBasell Industries | Polyolefin, Unspecified | Adsyl |