Durethan® BKV 130 GIT DUS008 900116
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS Corporation |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EADT6z_Durethan-BKV-130-GIT-DUS008-900116.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 30 % glass fibers, injection molding, improved impact strength, GIT/WIT |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.36 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 280°C, 2.00 mm 1 | 0.50 | -- | % | |
| Across Flow : 120°C, 2 hr, 2.00 mm 2 | 0.15 | -- | % | |
| Flow : 280°C, 2.00 mm 3 | 0.20 | -- | % | |
| Flow : 120°C, 2 hr, 2.00 mm 4 | 0.060 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 9000 | 5000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 160 | 95.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.4 | 7.5 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 8500 | 4900 | MPa | ISO 178/A |
| Flexural Stress 6 | ||||
| 3.5% Strain | 230 | 122 | MPa | ISO 178/A |
| 23°C | 256 | 145 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 7(23°C) | 4.1 | 6.3 | % |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6-HI, GR, 14-090, GF30 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Films | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Film Puncture Energy | ISO 6603-2 | |||
| -- 8 | 2.50 | -- | J | |
| -- 9 | 3.80 | -- | J | |
| Film Puncture Force | ISO 6603-2 | |||
| -- 10 | 770 | -- | N | |
| -- 11 | 935 | -- | N |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | 10 | kJ/m² | |
| 23°C | 15 | 20 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 65 | 60 | kJ/m² | |
| 23°C | 85 | 85 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 10 | 10 | kJ/m² | |
| 23°C | 15 | 15 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 60 | 55 | kJ/m² | |
| 23°C | 75 | 60 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 210 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 195 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 200 | -- | °C | ISO 306/B120 |
| Melting Temperature 12 | 220 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 2.0E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 9.0E-5 | -- | cm/cm/°C |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; MT 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; MT 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Pull Rate: 2 mm/min; 50% RH |
| 8 . | -30°C |
| 9 . | 23°C |
| 10 . | -30°C |
| 11 . | 23°C |
| 12 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 6604-5 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Sasol Polymers PE LT019 | Sasol Polymers | LDPE | Sasol Polymers PE |
| TERRAMAC TE-2000 | UNITIKA Plastics Division | PLA | TERRAMAC |
| Wondel® P PR0G4 | Nanjing Julong Engineering Plastics Co., LTD | PP, Unspecified | Wondel® P |
| VAMPAMID 66 2525 V0 | Vamp Tech | Nylon 66 | VAMPAMID |