InnoPlus HD3001C
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | PTT Global Chemical Public Company Limited |
| Trademark: | InnoPlus |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | E9TG68_InnoPlus-HD3001C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
InnoPlus HD3000C and HD3001C are high density polyethylene which are specially designed for beverage caps. Both grades have excellent organoleptic properties which prevent unpleasant odor and taste from cap or closure to transfer to water. They show good processability in either injection molding or compression molding machine. Additive InnoPlus HD3000C with slip agent. InnoPlus HD3001C without slip agent. Typical Application: Beverage caps for mineral, stilled, sparkling water and carbonated soft drink. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.954 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (25% Igepal, F50) | 24.0 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 62 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 25.5 | MPa | |
| Break | 31.4 | MPa | |
| Tensile Elongation (Break) | 800 | % | ASTM D638 |
| Apparent Bending Modulus | 775 | MPa | ASTM D747 |
| Flexural Modulus | 1110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 1 | 49 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 122 | °C | ASTM D1525 2 |
| Peak Melting Temperature | 130 | °C | ASTM D3418 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Temperature | 160 to 180 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 170 to 200 | °C | |
| Middle Temperature | 170 to 200 | °C | |
| Front Temperature | 170 to 200 | °C |
| Note Message | |
|---|---|
| 1 . | Partial Break |
| 2 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Tech™ Stat-Tech™ X0300-8001 EDS BK001 | PolyOne Corporation | PC | Stat-Tech™ |
| Staramide A28K | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| Elastollan® S 70 A | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| Gravi-Tech™ GRV-PB-069-BMX Natural | PolyOne Corporation | PEBA-Ether | Gravi-Tech™ |
| LNP™ LUBRICOMP™ DBL349E compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |