Capran® 512 LL
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Honeywell |
| Trademark: | Capran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | E9S1hE_Capran-512-LL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Capran® 512 LL is a heat-stabilized blown film produced from low lactam nylon-6 resin. It is recommended as bagging film for advanced composite fabrication and other high temperature applications where softness and workability are essential. Capran® 512 LL has excellent heat stability and resistance to pinholing. It can be used at temperatures up to 390°F (199°C) for typical composite cure cycle times. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Tensile Strength - MD | ASTM D882 | ||
| Yield | 31.0 | MPa | ASTM D882 |
| Fracture | 112 | MPa | ASTM D882 |
| Tensile Elongation - MD (Break) | 380 | % | ASTM D882 |
| Elmendorf Tear Strength - MD | 130 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Crystallization Temperature (DSC) | 218 - 220 | °C | ASTM D3418 |
| Additional Information |
|---|
| Dimensional Stability, ASTM D1204, 30 mins, 300°F:<2% shrinkage |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren Y1200 (Premium-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| VICOTE® F804Blk | Victrex plc | PEEK | VICOTE® |
| TPUCO® TPUI-L70 | Taiwan PU Corporation | TPU-Polyether | TPUCO® |
| Unilex™ UP 8020 | United Polychem | PP Homopolymer | Unilex™ |
| ANYPOL SE-160LL | SH Energy & Chemical | PS (EPS) | ANYPOL |