Mineralblend® PP-2800
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Colour Image Plastic Compound Sdn. Bhd. (CIPC) |
| Trademark: | Mineralblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | E8ngtg_Mineralblend-PP-2800.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Mineralblend® PP-2800 is a medium flow highly mica filled polypropylene homopolymer compound characterized by high stiffness and dimensional stability and additional low shrinkage properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 to 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 30.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 | % | ASTM D638 |
| Flexural Modulus | 5400 | MPa | ASTM D790 |
| Flexural Strength | 52.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 40 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 4.00 mm | 140 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm | 90.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 180 to 190 | °C | |
| Middle Temperature | 190 to 200 | °C | |
| Front Temperature | 200 to 210 | °C | |
| Nozzle Temperature | 210 to 220 | °C | |
| Processing (Melt) Temp | 190 to 220 | °C | |
| Mold Temperature | 60.0 to 70.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RABALON® MJ8301C | Mitsubishi Chemical Performance Polymers, Inc. | TPE | RABALON® |
| CALP 8803R | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| Latan 13 | LATI S.p.A. | Acetal (POM) Copolymer | Latan |
| Plaslube® PA6 HS L MB | Techmer Engineered Solutions | Nylon 6 | Plaslube® |
| Osterlene® HD0752 | Osterman & Company | HDPE | Osterlene® |