AvaSpire® AV-722 Datasheet,PAEK,Solvay Specialty Polymers-SHANGHAI SUSHENG

Message
AvaSpire® AV-722 is an unreinforced polyaryletherketone (PAEK) that offers improved economics relative to PEEK while retaining most of PEEK's key performance attributes. AV-722 resin has been formulated for applications requiring high chemical resistance and mechanical strength along with low moisture absorption and good barrier properties. These and other properties make this resin well-suited for applications in healthcare, transportation, electronics, chemical processing and other industries. Beige: AvaSpire® AV-722 BG 20

General Information
Features	Good dimensional stability Impact resistance, good Good chemical resistance Heat resistance, high ductility Flame retardancy
Uses	Films Gear Electrical/Electronic Applications Aircraft applications Seals Application in Automobile Field Fuel line Oil/Gas Supplies Medical/nursing supplies
RoHS Compliance	Contact manufacturer
Appearance	Beige
Forms	Particle
Processing Method	Film extrusion Wire & Cable Extrusion Machining Extrusion blow molding Thermoforming Fiber (spinning) extrusion Profile extrusion molding Injection blowing molding Injection molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.32	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (400°C/2.16 kg)	1.0	g/10 min	ASTM D1238
Molding Shrinkage ¹			ASTM D955
Flow : 3.18mm	0.80 - 1.0	%	ASTM D955
Transverse flow : 3.18mm	1.2 - 1.4	%	ASTM D955
Water Absorption (24 hr)	0.10	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	95		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus
-- ²	3700	MPa	ASTM D638
--	3900	MPa	ISO 527-2/1A/1
Tensile Stress
Yield	91.0	MPa	ISO 527-2/1A/50
-- ³	89.0	MPa	ASTM D638
Tensile Elongation
Yield ⁴	5.0	%	ASTM D638
Yield	4.5	%	ISO 527-2/1A/50
Fracture ⁵	25	%	ASTM D638
Fracture	25	%	ISO 527-2/1A/50
Flexural Modulus
--	3700	MPa	ASTM D790
--	3800	MPa	ISO 178
Flexural Strength
--	141	MPa	ASTM D790
--	138	MPa	ISO 178
Compressive Strength	112	MPa	ASTM D695
Shear Strength	79.0	MPa	ASTM D732
Poisson's Ratio	0.43		ASTM E132

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact
--	80	J/m	ASTM D256
--	7.0	kJ/m²	ISO 180
Unnotched Izod Impact	No Break		ASTM D4812, ISO 180

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load ⁶(1.8 MPa, Annealed, 3.20 mm)	161	°C	ASTM D648
Glass Transition Temperature	150	°C	ASTM D3418
Peak Melting Temperature ⁷	340	°C	ASTM D3418
CLTE - Flow (-50 to 50°C)	4.5E-5	cm/cm/°C	ASTM E831
Specific Heat			DSC
50°C	1410	J/kg/°C	DSC
200°C	1970	J/kg/°C	DSC
Thermal Conductivity	0.22	W/m/K	ASTM E1530

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.9E+17	ohms	ASTM D257
Volume Resistivity	3.1E+17	ohms·cm	ASTM D257
Dielectric Strength			ASTM D149
0.0500mm, amorphous film	170	kV/mm	ASTM D149
3.00 mm	19	kV/mm	ASTM D149
Dielectric Constant			ASTM D150
60 Hz	3.12		ASTM D150
1 MHz	3.06		ASTM D150
Dissipation Factor			ASTM D150
60 Hz	1.0E-3		ASTM D150
1 MHz	4.0E-3		ASTM D150

Flammability	Nominal Value	Unit	Test Method
Oxygen Index	40	%	ASTM D2863

Fill Analysis	Nominal Value	Unit
Melt Viscosity (400°C, 1000 sec^-1)	450	Pa·s

Injection instructions
Back Pressure: Minimum

Category:	PAEK , Polyaryletherketone
Manufacturer:	Solvay Specialty Polymers
Trademark:	AvaSpire®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	E846y7_AvaSpire-AV-722.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
SABIC® PP RA12MN40	Saudi Basic Industries Corporation (SABIC)	PP Random Copolymer	SABIC® PP
SCHULAMID® 6 MV HI	A. Schulman Europe	Nylon 6	SCHULAMID®
Mylar® EB-11 (500 guage)	DuPont Teijin Films U.S.	PET	Mylar®
Axiall PVC 8676	Axiall Corporation	PVC, Flexible	Axiall PVC
Esterlloy™ AT27	Asahi Kasei Chemicals Corporation	ABS Alloy	Esterlloy™