Desmopan® 588 E
| Category: | TPU-Ester/Ether , Thermoplastic Polyurethane Elastomer (Ester/Ether) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Desmopan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | E6eUvq_Desmopan-588-E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Extrusion- and injection molding grade; improved microbial resistance; Improved hydrolysis resistance; Application; Cable sheathings; Hoses, non-reinforced; Roof lining |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1150 | kg/m³ | ISO 1183 1 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 2 | ||
| Shore A, 3 sec | 88 | ||
| Shore D, 15 sec | 33 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 3 | DIN 53504 | ||
| Break, 23°C | 39.1 | MPa | |
| 10% Strain, 23°C | 2.00 | MPa | |
| 50% Strain, 23°C | 4.80 | MPa | |
| 100% Strain, 23°C | 6.30 | MPa | |
| 300% Strain, 23°C | 11.6 | MPa | |
| Tensile Strain 4(Break, 23°C) | 580 | % | DIN 53504 |
| Abrasion Resistance (23°C) | 60.0 | mm³ | ISO 4649-A |
| Tensile Storage Modulus | ISO 6721-1,-4 | ||
| -20°C | 165 | MPa | |
| 20°C | 29.0 | MPa | |
| 60°C | 20.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Resilience | 36 | % | ISO 4662 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 5 | 55 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 25 | % | |
| 70°C, 24 hr | 50 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Processing (Melt) Temp | 210 to 230 | °C | |
| Mold Temperature | 20.0 to 40.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Melt Temperature | 190 to 210 | °C |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | 200 mm/min |
| 4 . | 200 mm/min |
| 5 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPRAN® LFT PA A1340 | SAMBARK | Nylon 66 | SUPRAN® LFT PA |
| FHR Polypropylene 21N2A | Flint Hills Resources, LP | PP Homopolymer | FHR Polypropylene |
| EPLAMID 6 GCV2 20 NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 6 | EPLAMID 6 |
| Plaslube® POM CO GF30 TL5 | Techmer Engineered Solutions | Acetal (POM) Copolymer | Plaslube® |
| Sumiliteresin® PR-51649 BI | SBHPP | Phenolic | Sumiliteresin® |