RIALFLAME H V2L 15 H 20 TD
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | RIALTI Srl |
| Trademark: | RIALFLAME |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | E6HqUU_RIALFLAME-H-V2L-15-H-20-TD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene self-extingusihing compound, homopolymer 20% talc filled; classifiable according to the norms of UL-94, V-2; low halogen content. Free from PBDE. Free from antimony and heavy metals. Thermal stabilization for use at high process temperatures. High flowability and stiffness, specific for applications where good planarity and dimensional stability with contained shrinkage are required. Available in the versions natural and colored as per sample. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.2 | % | |
| Flow | 1.2 | % | |
| Ash Content | 20 | % | ISO 3451 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Accelerated Oven Aging (150°C) | 16.7 | day | ISO 4577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 76 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/20 | ||
| Yield, 23°C | 31.0 | MPa | |
| Break, 23°C | 23.0 | MPa | |
| Tensile Strain | ISO 527-2/20 | ||
| Yield, 23°C | 5.0 | % | |
| Break, 23°C | 30 | % | |
| Flexural Modulus 1(23°C) | 2500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 46.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 34 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -20°C | 2.2 | kJ/m² | |
| 23°C | 2.6 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 61.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 92.0 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 335 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-2 | ||
| 3.00 mm | V-2 | ||
| Glow Wire Flammability Index 2 | IEC 60695-2-12 | ||
| 1.00 mm | 850 | °C | |
| 2.00 mm | 850 | °C | |
| 4.00 mm | 850 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 725 | °C | |
| 2.00 mm | 725 | °C | |
| 4.00 mm | 725 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 180 to 200 | °C | |
| Mold Temperature | 30.0 to 40.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | IDONEO |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene HP531-678UV | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| SMOKEGUARD™ IV 1320 NATURAL | AlphaGary | PVC, Unspecified | SMOKEGUARD™ IV |
| Sylvin 9223-55 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Iupital® FC2020H | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |
| Delon 6055 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TEEE | Delon |