Starex VE-1870 U
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | E6GygL_StarexVE1870U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Starex VE-1870 U is a high impact polystyrene product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 8.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 22.0 | MPa | ASTM D638 |
| Flexural Modulus 2 | 1800 | MPa | ASTM D790 |
| Flexural Strength 3 | 28.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 98 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 72.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 82.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.7 mm | V-0 | UL 94 | |
| 3.4 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 60 | °C | |
| Hot air dryer | 60 | °C | |
| Drying Time | |||
| -- | 4.0 - 6.0 | hr | |
| Hot air dryer | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | < 0.10 | % | |
| Rear Temperature | 180 - 210 | °C | |
| Middle Temperature | 210 | °C | |
| Front Temperature | 210 | °C | |
| Nozzle Temperature | 220 | °C | |
| Mold Temperature | 60 - 80 | °C | |
| Injection Pressure | 68.6 - 206 | MPa | |
| Back Pressure | 0.981 | MPa | |
| Screw Speed | 40 | rpm |
| Injection instructions |
|---|
| Hot Runner Manifold Temperature: 210°CHot Runner Valve Nozzle Temperature: 210°C |
| Note Message | |
|---|---|
| 1 . | 20 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 2.8 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SRF3812 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Sinvicomp SBB3715 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Formolene® L42009E2 | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene® |
| POLYFORM C 2,5 | POLYMA Kunststoff GmbH & Co. KG | Acetal (POM) Homopolymer | POLYFORM |
| Hostaform® C 13021 LS | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |