RTP 499 X 133941
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | E5mq33_RTP-499-X-133941.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame Retardant |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2070 | MPa | ASTM D638 |
| Tensile Strength | 29.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 10 | % | ASTM D638 |
| Flexural Modulus | 2070 | MPa | ASTM D790 |
| Flexural Strength | 46.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 1000 | J/m | ASTM D4812 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 210 to 249 | °C | |
| Mold Temperature | 37.8 to 65.6 | °C | |
| Injection Pressure | 68.9 to 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Network Polymers PC 1011 | Network Polymers, Inc. | PC | Network Polymers PC |
| ALTECH® PA66 A 2015/310 GF15 IM | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| ENGAGE™ 8180 | The Dow Chemical Company | TPO (POE) | ENGAGE™ |
| HiFill® PA6 0348 | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Karina CRYSTAL PVC COMP. E 75/325-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |