VITAMIDE® BB74BG6579
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | VITAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | E5Oyw6_VITAMIDE-BB74BG6579.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VITAMIDE® BB74BG6579 is a Polyamide 6 (Nylon 6) product filled with 20% glass bead. It is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792, ISO 1183 |
| Water Absorption (23°C, 24 hr) | 1.1 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 75.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 13 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 3300 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 140 | MPa | ISO 178 |
| Break | 140 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 35 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 197 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 88.0 | °C | ASTM D648, ISO 75-2/A |
| Peak Melting Temperature | 218 | °C | ASTM D2117, ISO 1218 |
| CLTE - Flow | 6.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 6.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 14 | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index (Solution A) | 450 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen PP567P | LyondellBasell Industries | PP Homopolymer | Moplen |
| Axiall PVC 1901 Clear 7002 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| LEXAN™ ML3729 resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| Karina BLACK PVC COMPOUND -E CAK 65/48/ 1-CS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Jam HP-LL18XF5N | Jam Petrochemical Company | LLDPE | Jam |