Generic PE, Unspecified
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | E4hu3u_Generic-PE-Unspecified.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PE, Unspecified This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.898 - 0.960 | g/cm³ | ASTM D792 |
| 23°C | 0.900 - 0.964 | g/cm³ | ISO 1183 |
| -- | 0.896 - 0.964 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/2.16 kg | 0.20 - 7.7 | g/10 min | ASTM D1238 |
| 190°C/2.16 kg | 0.20 - 9.2 | g/10 min | ISO 1133 |
| Water Absorption (23°C, 24 hr) | 9.8E-3 - 0.011 | % | ASTM D570 |
| Environmental Stress-Cracking Resistance (23°C) | 1.00 - 1000 | hr | ASTM D1693 |
| Carbon Black Content | 40 - 45 | % | ASTM D1603 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (23°C) | 46 - 96 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 350 - 2220 | MPa | ASTM D638 |
| 23°C | 329 - 902 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 10.0 - 24.4 | MPa | ASTM D638 |
| Yield, 23°C | 10.8 - 27.4 | MPa | ISO 527-2 |
| Fracture, 23°C | 10.7 - 26.7 | MPa | ASTM D638 |
| Fracture, 23°C | 12.0 - 19.2 | MPa | ISO 527-2 |
| 23°C | 11.0 - 19.8 | MPa | ASTM D638 |
| Tensile Strain | |||
| Yield, 23°C | 5.6 - 19 | % | ISO 527-2 |
| Fracture, 23°C | 36 - 830 | % | ASTM D638 |
| Fracture, 23°C | 1.0 - 530 | % | ISO 527-2 |
| Apparent Bending Modulus (23°C) | 97.0 - 171 | MPa | ASTM D747 |
| Flexural Modulus | |||
| 23°C | 101 - 1030 | MPa | ASTM D790 |
| 23°C | 80.0 - 1160 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 8.00 - 37.9 | MPa | ASTM D790 |
| 23°C | 18.0 - 45.0 | MPa | ISO 178 |
| Coefficient of Friction | 0.10 - 0.50 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 23 - 45 | µm | |
| secant modulus | ASTM D882 | ||
| MD | 108 - 185 | MPa | ASTM D882 |
| TD | 105 - 225 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 4.80 - 20.3 | MPa | ASTM D882 |
| TD : Yield | 4.20 - 11.1 | MPa | ASTM D882 |
| MD : Fracture | 20.7 - 60.7 | MPa | ASTM D882 |
| TD : Fracture | 20.2 - 62.7 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 350 - 720 | % | ASTM D882 |
| TD : Fracture | 580 - 720 | % | ASTM D882 |
| Dart Drop Impact (23°C) | 55 - 110 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 100 - 360 | g | ASTM D1922 |
| TD | 220 - 600 | g | ASTM D1922 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 19 - 470 | J/m | ASTM D256 |
| 23°C | 2.0 - 6.8 | kJ/m² | ISO 180 |
| Tensile Impact Strength (23°C) | 285 | kJ/m² | ISO 8256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 69.3 - 70.2 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 58.0 - 82.3 | °C | ISO 75-2/B |
| Brittleness Temperature | -75.0 - -48.8 | °C | ASTM D746 |
| Vicat Softening Temperature | |||
| -- | 68.4 - 125 | °C | ASTM D1525 |
| -- | 83.9 - 126 | °C | ISO 306 |
| Peak Melting Temperature | |||
| -- | 117 - 128 | °C | ASTM D3418 |
| -- | 114 - 125 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0 - 2.5E+13 | ohms | ASTM D257 |
| Volume Resistivity | |||
| 23°C | 3.6 - 1.0E+16 | ohms·cm | ASTM D257 |
| 23°C | 25 - 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Constant (23°C) | 2.30 - 3.70 | ASTM D150 | |
| Dissipation Factor (23°C) | 3.0E-4 - 0.010 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 30 - 32 | % | ISO 4589-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | 58 - 88 | ASTM D2457 | |
| Haze | 2.2 - 7.3 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.9 - 81.0 | °C | |
| Drying Time | 1.0 - 4.0 | hr | |
| Processing (Melt) Temp | 105 - 232 | °C | |
| Mold Temperature | 37.8 - 47.6 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PE, UnspecifiedThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 40.0 - 69.3 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Cylinder Zone 1 Temp. | 83.4 - 202 | °C | |
| Cylinder Zone 2 Temp. | 83.4 - 212 | °C | |
| Cylinder Zone 3 Temp. | 83.5 - 220 | °C | |
| Cylinder Zone 4 Temp. | 83.8 - 151 | °C | |
| Cylinder Zone 5 Temp. | 83.8 - 223 | °C | |
| Melt Temperature | 109 - 228 | °C | |
| Die Temperature | 115 - 232 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PE, UnspecifiedThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ PPC-40G Black | PolyOne Corporation | PP Copolymer | Maxxam™ |
| Sinvicomp SSG6066 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Unigel PS U249 | Unigel Plásticos | PS (GPPS) | Unigel PS |
| Hanwha Total PP RB73T | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Kumho KNB 25LM | Korea Kumho Petrochemical Co., Ltd. | NBR | Kumho KNB |