Vipel® F774-PTA-25
| Category: | Polyester Alloy , Polyester Alloy |
| Manufacturer: | AOC, L.L.C. |
| Trademark: | Vipel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | E4QFng_Vipel-F774-PTA-25.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vipel® Corrosion High-Cross Linked, Terephthalic Polyester Resin Vipel® F774-PTA series is a high cross-linked terephthalic polyester resin. Vipel F774 series resin are recognized by underwriters laboratories for meeting the requirements of UL 1316 and UL 1746 Part II and Part III. Vipel® F774 series resin were developed to meet the demanding requirements of underground petroleum storage tanks that contain oxygenated fuels UL Recognition AOC's Vipel® F774 series resins are recognized by UL for meeting the requirements of UL 1316 and UL 1746 Part II and Part III. Corrosion Resistance Vipel® F774 series resins provide excellent corrosion resistance when used in contact with inorganic and organic acids. Solvent resistance is field-proven for many fuels including gasoline, kerosene, heating oil and crude oils. Refer to AOC's "Corrosion Resistant Resin Guide" for corrosion resistance information or for questions regarding suitability of a resin to any particular chemical environment contact AOC. Versatile Suitable for various fabricating methods such as hand lay-up, spray-up, filament winding, etc. Food and Drug All resins in this datasheet are manufactured from raw materials that are listed in FDA regulation Title 21 CFR 177.2420. It is the fabricator's responsibility to also be sure that the final composite is well cured. All composites used for FDA applications should be post cured at 180°F for at least 4 hours. After post curing it should be washed with soap and water and rinsed. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Barcol Hardness | 46 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3860 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 80.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.7 | % | ASTM D638 |
| Flexural Modulus | 3860 | MPa | ASTM D790 |
| Flexural Strength | 119 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 146 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Mix Viscosity 1(25°C) | 700 | cP | |
| Post Cure Time (82°C) | 4.0 | hr | |
| Exotherm | |||
| Gel to Peak | 11.0 | min | |
| Peak | 220 | °C | |
| Gel Time (25°C) 2 | 25.0 | min |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| HAP Content | 45 | % | |
| Thixotropic Index (25°C) 3 | 2.00 |
| Note Message | |
|---|---|
| 1 . | Brookfield RVT viscosity spindle 2 at 20 rpm |
| 2 . | Gel time with 1.0% MEKP (100 gram mass) |
| 3 . | 2/20 Thix Index |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1207-70A | RTP Company | TPU-Polyester | RTP |
| Polymer-E EV102 | Asia Polymer Corporation (APC) | EVA | Polymer-E |
| Generic Silicone Rubber, RTV-2 | Generic | Silicone Rubber, RTV-2 | Generic |
| Karina CLEAR PVC COMPOUND 800-204-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| TARFLON™ RE1900 | Idemitsu Kosan Co., Ltd. | PC | TARFLON™ |