Makroblend® UT235 M
| Category: | PC+PET , Polycarbonate + PET |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Makroblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | E25G0Z_Makroblend-UT235-M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| (PC+PET)-blend, mineral filled, easy flow, low coefficient of linear thermal expansion, easy release, injection molding. Molded parts from UT235M having exceptional dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.34 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (270°C/5.0 kg) | 39.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 2577 | ||
| Across Flow : 270°C, 3.00 mm | 0.50 to 0.60 | % | |
| Flow : 270°C, 3.00 mm | 0.50 to 0.60 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.40 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 4500 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 68.0 | MPa | |
| Break, 23°C | 67.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 3.5 | % | |
| Break, 23°C | 4.0 | % | |
| Flexural Modulus 2(23°C) | 4650 | MPa | ISO 178 |
| Flexural Stress 3 | ISO 178 | ||
| 23°C | 115 | MPa | |
| 3.5% Strain, 23°C | 110 | MPa | |
| Flexural Strain at Flexural Strength 4(23°C) | 5.0 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 85 | kJ/m² | |
| 23°C | 85 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180 | ||
| -30°C | 85 | kJ/m² | |
| 23°C | 85 | kJ/m² | |
| Multi-Axial Instrumented Impact Energy (23°C) | 36.0 | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force (23°C) | 4500 | N | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 128 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 114 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 139 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 85°C | 4.5E-5 | cm/cm/°C | |
| Transverse : 23 to 85°C | 4.8E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | 150x105x3 mm, 70°C MT, 600 bar |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHLEN CM313 | DAEHA Co., LTD | PP, Unspecified | TECHLEN |
| Durez® 33458 | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| LOXIM 841 02T HB | LOXIM Industries Private Limited | PP Copolymer | LOXIM |
| LUVOCOM® 1106-7940/GY/EM | Lehmann & Voss & Co. | PEI | LUVOCOM® |
| ALTECH® ABS A 1000/106 GY2093-07LS | ALBIS PLASTIC GmbH | ABS | ALTECH® ABS |