PENTAMID AHT H1 ungefärbt
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTAMID AHT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | E1iVYH_PENTAMID-AHT-H1-ungef-rbt.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 4.6 |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.18 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 2.3 | -- | % | |
| Flow | 2.2 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 10 | -- | % | |
| Equilibrium, 23°C, 50% RH | 3.6 | -- | % | |
| Viscosity Number | 160 | -- | cm³/g | ISO 307 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 170 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3200 | 1000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 100 | 55.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 8.0 | 25 | % | ISO 527-2 |
| Flexural Modulus | 3250 | -- | MPa | ISO 178 |
| Flexural Stress | 125 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | 35 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 285 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 160 | -- | °C | ISO 75-2/A |
| Melting Temperature | 295 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Electric Strength (1.00 mm) | 25 | -- | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.50 | -- | IEC 60250 | |
| Comparative Tracking Index | 450 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Type | PA46, MHR, 16-030 N | PA46, MHR, 16-030 N | ISO 1874 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.17 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 290 to 315 | °C | |
| Middle Temperature | 305 to 320 | °C | |
| Front Temperature | 305 to 315 | °C | |
| Processing (Melt) Temp | 310 | °C | |
| Mold Temperature | 100 | °C | |
| Injection Pressure | 65.0 | MPa | |
| Holding Pressure | 35.8 | MPa | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEFTEKHIM PP 1500H (S30G) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| Akulon® Ultraflow K-FG0 | DSM Engineering Plastics | Nylon 6 | Akulon® Ultraflow |
| Baytec® MS-041 (HQEE) | Covestro - PUR | PUR-Ester/MDI | Baytec® |
| Karina BLACK PVC COMPOUND -E CAK 85-48/ 1 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PLEXIGLAS® Film White WF002 | Evonik Industries AG | Film, PMMA | PLEXIGLAS® Film |