Boda BDF401P
| Category: | Fluorelastomer , Fluoroelastomer |
| Manufacturer: | Chenguang Fluoro & Silicone Elastomers Co., Ltd. |
| Trademark: | Boda |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | E0YlYN_Boda-BDF401P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BDF401P is a medium viscosity curative incorporated fluoroelastomer copolymer. This grade is well suited for application where good rheological properties and excellent compression set resistance are required. BDF401P can be compounded to meet the major fluoroelastomer specifications. BDF401P can be used for compression molding of O-rings and gaskets. It can be mixed using typical fluoroelastomer compounding ingredients. Mixing can be accomplished with two-roll mills or internal mixers. Finished goods can be produced by a variety of rubber processing methods. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.80 | g/cm³ | |
| Mooney Viscosity (ML 1+10, 121°C) | 40 | MU | |
| Fluorine Content | 66 | % | |
| Solubility | LMW Ketones and esters |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| MH 1(177°C) | 2.50 | N·m | |
| ML 2(177°C) | 0.300 | N·m | |
| t'90 3(177°C) | 2.4 | min | |
| ts2 4(177°C) | 1.2 | min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 5(Shore A) | 78 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 6(Yield) | 14.0 | MPa | ASTM D412 |
| Tensile Elongation 7(Break) | 190 | % | ASTM D412 |
| Compression Set (200°C, 70 hr) | 15 | % | ASTM D395B |
| Additional Information |
|---|
| Test Compound: Polymer: 100 MT Black (N990): 30 phr MgO: 3 phr Ca(OH)2: 6 phr Curing Condition: Press: 10 min at 170°C Oven: 24 hr at 230°C |
| Note Message | |
|---|---|
| 1 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 2 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 3 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 4 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 5 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| 6 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| 7 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Witcom PE 4L1 | Witcom Engineering Plastics B.V. | PE, Unspecified | Witcom PE |
| Network Polymers PP PPH 30 0500 GF20 | Network Polymers, Inc. | PP Homopolymer | Network Polymers PP |
| AIE PET 40G8 | Asia International Enterprise (Hong Kong) Limited | PET | AIE PET |
| Karina CLEAR PVC COMPOUND 70/201-D-AT-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 9067-90 White 125 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |