LNP™ COLORCOMP™ D1000FL compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ COLORCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DzD439_LNP-COLORCOMP-D1000FL-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP COLORCOMP D1000FL is an unfilled compound based on Polycarbonate resin. Added features of this grade are: Superior Molding, Low Extractible. Also known as: LNP* COLORCOMP* Compound D-1000 LE SM Product reorder name: D1000FL |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Water Absorption (24 hr, 50% RH) | 0.30 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2390 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 64.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Yield) | 6.0 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 137 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 125 | °C | ISO 75-2/Af |
| Thermal Conductivity | 0.17 | W/m/K | ASTM E1530 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Syncure™ S1000B | PolyOne Corporation | XLPE | Syncure™ |
| ASI POLYPROPYLENE PP 3369-01 | A. Schulman Inc. | PP Homopolymer | ASI POLYPROPYLENE |
| 3M™ Dyneon™ Fluoroelastomer FC 2176Z | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |
| GAPEX® RPP25EB74HB GRAY | Ferro Corporation | PP Homopolymer | GAPEX® |
| LGE 624 | LG Polymers India Pvt. Ltd. | PS (EPS) | LGE |