CYCOLOY™ CM6210 resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Dz55Ye_CYCOLOYCM6210resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CYCOLOY resin CM6210 is a high-modulus flame retardant PC/ABS with non-brominated and non-chlorinated FR system. It can be used for extrusion & thermoforming applications and also for injection molding applications where higher stiffness is needed. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.28 | g/cm³ | ASTM D792 |
| -- | 1.27 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 12 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 9.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.60 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.30 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.10 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 98 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3570 | MPa | ASTM D638 |
| -- | 3660 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 64.0 | MPa | ASTM D638 |
| Yield | 59.7 | MPa | ISO 527-2/5 |
| Yield | 63.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 50.0 | MPa | ASTM D638 |
| Fracture | 65.0 | MPa | ISO 527-2/5 |
| Fracture | 50.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 4.9 | % | ASTM D638 |
| Yield | 3.6 | % | ISO 527-2/5 |
| Yield | 3.5 | % | ISO 527-2/50 |
| Fracture 5 | 80 | % | ASTM D638 |
| Fracture | 100 | % | ISO 527-2/5 |
| Fracture | 97 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 3500 | MPa | ASTM D790 |
| -- 7 | 3560 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 106 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 45 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 90 | J/m | ASTM D256 |
| 23°C | 500 | J/m | ASTM D256 |
| -30°C 10 | 10 | kJ/m² | ISO 180/1A |
| 23°C 11 | 45 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 45.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 100 mm span 12 | 99.0 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 3.20mm | 90.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span 13 | 89.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 106 | °C | ASTM D1525 14 |
| -- | 112 | °C | ISO 306/B50 |
| -- | 114 | °C | ISO 306/B120 |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 75°C | Pass | IEC 60695-10-2 | |
| 95°C 15 | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 5.7E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 5.2E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 23 to 60°C | 5.2E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 7.0E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.30 | W/m/K | ISO 8302 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | IEC 60243-1 | ||
| 0.800mm, in oil | 38 | kV/mm | IEC 60243-1 |
| 1.60mm, in oil | 26 | kV/mm | IEC 60243-1 |
| 3.20mm, in oil | 17 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 2.90 | IEC 60250 | |
| 60 Hz | 2.90 | IEC 60250 | |
| 1 MHz | 2.80 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 3.0E-3 | IEC 60250 | |
| 60 Hz | 3.0E-3 | IEC 60250 | |
| 1 MHz | 4.0E-3 | IEC 60250 | |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 87.8 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 182 - 227 | °C | |
| Cylinder Zone 2 Temp. | 188 - 232 | °C | |
| Cylinder Zone 3 Temp. | 204 - 241 | °C | |
| Cylinder Zone 4 Temp. | 210 - 243 | °C | |
| Adapter Temperature | 210 - 243 | °C | |
| Melt Temperature | 221 - 243 | °C | |
| Die Temperature | 210 - 243 | °C |
| Extrusion instructions |
|---|
| Drying Time (Cumulative): 12 hrsMinimum Moisture Content: 0.04 %Roll Stack Temp - Bottom: 66 - 88 °CRoll Stack Temp - Middle: 71 - 93 °CRoll Stack Temp - Top: 71 - 99 °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*3 sp=62mm |
| 10 . | 80*10*3 |
| 11 . | 80*10*3 |
| 12 . | 120*10*4 mm |
| 13 . | 120*10*4 mm |
| 14 . | 标准 B (120°C/h), 载荷2 (50N) |
| 15 . | Approximate maximum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| McCann PP M10TCPP10 | McCann Plastics Inc. | PP Copolymer | McCann PP |
| Sinvicomp SIZ4508A | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| StarTUFF TF 75-LR-1 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | StarTUFF |
| Fainplast PVC GS 82/SN | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Plenco 02311 (Transfer) | Plastics Engineering Co. | Phenolic | Plenco |