Kingfa API-CG318
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DydgsX_Kingfa-API-CG318.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa API-CG318 is a polypropylene material, and its filler is glass fiber reinforced material. This product is available in the Asia-Pacific region and is processed by injection molding. The main features of Kingfa API-CG318 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 - 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 0.90 | % | Internal method |
| Flow direction | 0.30 | % | Internal method |
| Ash Content (850°C) | 30 | % | ISO 3451-1 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 108 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 65.0 | MPa | ISO 527-2/10 |
| Tensile Strain (Break) | 3.2 | % | ISO 527-2/10 |
| Flexural Modulus 1 | 4500 | MPa | ISO 178 |
| Flexural Stress 2 | 95.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 10 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 4.00mm span | 150 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 140 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 180 - 200 | °C | |
| Middle Temperature | 200 - 230 | °C | |
| Front Temperature | 220 - 240 | °C | |
| Processing (Melt) Temp | 220 - 245 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.350 | MPa |
| Injection instructions |
|---|
| Processing Temp. Limit: 260°C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PC-FR2A-D-(color)-3 | Polymer Resources Ltd. | PC | PRL |
| DOW™ LDPE 5004I | The Dow Chemical Company | LDPE | DOW™ LDPE |
| Clariant Nylon 6/6 PA-113N40 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Formolene® 5143C | Formosa Plastics Corporation, U.S.A. | PP Homopolymer | Formolene® |
| Polifor® E 12 TR/10 NATURALE Y1 | SO.F.TER. SPA | PP, Unspecified | Polifor® |