Hostacom EKC 265N
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DyLTsE_Hostacom-EKC-265N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hostacom EKC 265N is a 20% mineral filled PP compound. Excellent scratch and mar properties, very low stress whitening. High flow, good stiffness/impact balance. High UV-resistance. Low odor, fogging & carbon emission. Used for interior trim applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 16 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 18.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.90 to 1.1 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant | 1950 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 18.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 5.0 | % | ISO 527-2/50 |
| Flexural Modulus - Secant | 1900 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 3.0 | kJ/m² | |
| 0°C | 6.0 | kJ/m² | |
| 23°C | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 35 | kJ/m² | |
| 0°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 56.0 | °C | ISO 75-2/A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4000 TFE 10 | RTP Company | PPA | RTP |
| Sup-tech P620 | Shanghai Suptech Engineering Plastics Co. Ltd. | PP, Unspecified | Sup-tech |
| Torelina® A503-X05 | Toray Resin Company | PPS | Torelina® |
| Karina BLACK PVC COMPOUND 105900-48/1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ STAT-KON™ LX00486C compound | SABIC Innovative Plastics | PEEK | LNP™ STAT-KON™ |