MAXAMID™ EPDM66G14-WT
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Pier One Polymers, Inc. |
| Trademark: | MAXAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DxkK8b_MAXAMID-EPDM66G14-WT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MAXAMID™ EPD66G14 is available with internal and external lubricants, UV stabilized and other modifications. Further information and details are available upon request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 96.5 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 10 | % | ASTM D638 |
| Flexural Modulus (23°C) | 3310 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 138 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 210 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 207 | °C | ASTM D648 |
| Melting Temperature | 255 | °C | DSC |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | < 0.20 | % | |
| Processing (Melt) Temp | 290 to 305 | °C | |
| Mold Temperature | 65.0 to 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Network Polymers SMMA MS 200 | Network Polymers, Inc. | Acrylic (SMMA) | Network Polymers SMMA |
| 4MID® 9B22240 | 4Plas | Nylon 6 | 4MID® |
| DAUNYL 66 AV | Daunia Trading srl | Nylon 66 | DAUNYL |
| GELOY™ FXW751SK resin | SABIC Innovative Plastics | ASA+PC | GELOY™ |
| Plaslube® PA6/6 GF33 TL10 HS | Techmer Engineered Solutions | Nylon 66 | Plaslube® |