SABIC® PPcompound 37T1020
| Category: | PP, Unspecified , Polypropylene Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Dxb786_SABICPPcompound37T1020.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC® PPCOMPOUND 37T1020 is a general purpose, talc filled, heat stabilized copolymer polypropylene compound. This compound exhibits high impact and high flow, and is suitable for injection molding applications. The IMDS ID is 16161338. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.05 | g/cm³ | ASTM D792 |
| -- | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 71 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2450 | MPa | ASTM D638 |
| -- | 2760 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 25.0 | MPa | ASTM D638 |
| Yield | 28.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 17.0 | MPa | ASTM D638 |
| Fracture | 25.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 4 | 3.7 | % | ASTM D638 |
| Yield | 3.5 | % | ISO 527-2/50 |
| Fracture 5 | 33 | % | ASTM D638 |
| Fracture | 45 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 64.0mm span 6 | 2840 | MPa | ISO 178 |
| 50.0mm span 7 | 2350 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C 8 | 1.4 | kJ/m² | ISO 179/1eA |
| 23°C 9 | 3.3 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.20 mm 10 | 52 | J/m | ASTM D256 |
| -30°C 11 | 1.7 | kJ/m² | ISO 180/1A |
| 0°C 12 | 3.5 | kJ/m² | ISO 180/1A |
| 23°C 13 | 3.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact 14(23°C, 3.20 mm) | 850 | J/m | ASTM D4812 |
| Instrumented Dart Impact 15(23°C, Energy at Peak Load) | 3.93 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 116 | °C | ASTM D648 |
| 0.45 MPa, not annealed 16 | 110 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 3.20mm | 60.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed 17 | 69.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 145 | °C | ISO 306/A50 |
| Coefficient of Linear Thermal Expansion | ISO 11359-2 | ||
| Flow : -30 to 100°C | 66.6 | µm/Mk | ISO 11359-2 |
| Transverse : -30 to 100°C | 128 | µm/Mk | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 190 - 230 | °C | |
| Middle Temperature | 200 - 250 | °C | |
| Front Temperature | 210 - 270 | °C | |
| Nozzle Temperature | 210 - 270 | °C | |
| Processing (Melt) Temp | 210 - 270 | °C | |
| Mold Temperature | 15.0 - 60.0 | °C | |
| Back Pressure | 1.00 - 1.50 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4mm, Cut |
| 9 . | 80*10*4 mm, Cut |
| 10 . | 63.5*12.7*3.2mm, Cut |
| 11 . | 80*10*4mm, Cut |
| 12 . | 80*10*4mm, Cut |
| 13 . | 80*10*4mm, Cut |
| 14 . | 63.5*12.7*3.2mm, Cut |
| 15 . | 2.20 m/sec |
| 16 . | 80*10*4mm, Cut |
| 17 . | 80*10*4mm, Cut |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 K TFE 15 | RTP Company | PARA | RTP |
| Spartech Polycom SC5-4530U | Spartech Polycom | PP Copolymer | Spartech |
| Nanguang TPU S-90AX | Fujian Nanguang Light Industry Co., Ltd. | TPU, Unspecified | Nanguang TPU |
| AKROMID® A3 GF 40 1 L black (4671) | AKRO-PLASTIC GmbH | Nylon 66+PP | AKROMID® |
| LONGLITE® PMC T391 | CCP Group | Phenolic | LONGLITE® PMC |