4PROP® 5C10800
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | 4Plas |
| Trademark: | 4PROP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DxG1nO_4PROP-5C10800.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4PROP 5C10800 is a MFI 10 to 15 Recycled Copolymer Polypropylene |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.908 | g/cm³ | ISO 1183 |
| Apparent Density | 0.53 - 0.58 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 12 | g/10 min | ISO 1133 |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.020 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1300 | MPa | ISO 527-2/5 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 22.0 | MPa | ISO 527-2/5 |
| Fracture, 23°C | 28.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 50 | % | ISO 527-2/5 |
| Flexural Modulus 2(23°C) | 1000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 4.0 | kJ/m² | ISO 180/1A |
| 23°C | 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 88.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 67.0 | °C | ISO 306/B |
| Melting Temperature 3 | 165 | °C | ISO 11357 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 650 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 - 240 | °C | |
| Mold Temperature | 20.0 - 50.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 40.0 - 80.0 | MPa | |
| Screw Speed | 400 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 20 - 60 °CBack Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 24 Hrs |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarnoform® 300 HI4 | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| Axiall PVC 8723 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| LNP™ FARADEX™ ES003E compound | SABIC Innovative Plastics | PEI | LNP™ FARADEX™ |
| Sylvin 802-88 White 1523 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 5145-70 Clear Green 3125 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |