Razalen® R121 TR5
| Category: | PP+EPDM , Polypropylene + EPDM Rubber |
| Manufacturer: | Razin™ Engineering Plastics |
| Trademark: | Razalen® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Dx40yW_Razalen-R121-TR5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Razalen R121TR5 is a rubber modified injection grade black color polypropylene reinforced with 5% Talc. It combines excellent toughness as well as excellent processability, chemical, and fatigue resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.910 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.95 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 18.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 50 | % | ASTM D638 |
| Flexural Modulus | 1910 | MPa | ASTM D790 |
| Flexural Strength | 26.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 30 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 90.0 | °C | |
| 1.8 MPa, Unannealed | 45.0 | °C | |
| Vicat Softening Temperature | 124 | °C | ASTM D1525 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 180 to 220 | °C | |
| Middle Temperature | 190 to 220 | °C | |
| Front Temperature | 200 to 220 | °C | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 30.0 to 60.0 | °C | |
| Injection Pressure | 50.0 to 150 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E580 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Tarnoform® 300 MW6 | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| ADENE OCZE | A.D. Compound spa | PP Homopolymer | ADENE |
| AURAPENE PPTF20BK | Aurora Manufacturing Ltd | TPO | AURAPENE |
| Karina CRYSTAL PVC COMPOUND -E 75/320-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |