Elastollan® 1185 A 10 FC
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | BASF Polyurethanes GmbH |
| Trademark: | Elastollan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Dwt3IR_Elastollan1185A10FC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Thermoplastic Polyether-Polyurethane with outstanding hydrolysis resistance, low temperature flexibility and high resistance to micro-organisms. General suitability for food contact related applications in FDA and EU regulated markets (please see food contact information) |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183/A |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | DIN 7619-1 | ||
| Shao A, 3 seconds | 87 | DIN 7619-1 | |
| Shaw D, 3 seconds | 36 | DIN 7619-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 25.0 | mm³ | ISO 4649-A |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | DIN 53504-S2 | ||
| 20% strain | 2.50 | MPa | DIN 53504-S2 |
| 100% strain | 6.00 | MPa | DIN 53504-S2 |
| 300% strain | 10.0 | MPa | DIN 53504-S2 |
| Tensile Stress | DIN 53504-S2 | ||
| Yield | 45.0 | MPa | DIN 53504-S2 |
| Yield 1 | 32.0 | MPa | DIN 53504-S2 |
| Tensile Elongation 2(Break) | 600 | % | DIN 53504-S2 |
| Tear Strength 3 | 70 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 25 | % | ISO 815 |
| 70°C, 24 hr | 45 | % | ISO 815 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1 | ||
| -30°C | No Break | ISO 179/1 | |
| 23°C | No Break | ISO 179/1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 - 90 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40 | °C | |
| Rear Temperature | 205 - 215 | °C | |
| Middle Temperature | 210 - 225 | °C | |
| Front Temperature | 215 - 225 | °C | |
| Nozzle Temperature | 220 - 230 | °C | |
| Processing (Melt) Temp | 215 - 225 | °C | |
| Mold Temperature | 20 - 40 | °C | |
| Injection Rate | Slow | ||
| Back Pressure | 5.00 - 15.0 | MPa | |
| Screw L/D Ratio | 18.0:1.0 to 22.0:1.0 | ||
| Screw Compression Ratio | 2.0 : 1.0 - 3.0 : 1.0 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 - 90 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Cylinder Zone 1 Temp. | 155 - 175 | °C | |
| Cylinder Zone 2 Temp. | 165 - 185 | °C | |
| Cylinder Zone 3 Temp. | 175 - 195 | °C | |
| Cylinder Zone 4 Temp. | 185 - 205 | °C | |
| Adapter Temperature | 190 - 210 | °C | |
| Die Temperature | 185 - 205 | °C |
| Note Message | |
|---|---|
| 1 . | after storage in water at 80°C for 42 days |
| 2 . | after storage in water at 80°C for 42 days |
| 3 . | Method B, right-angle specimen (cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® 5014L AB305 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Homopolymer | POLYPRO® |
| Sumikon® PM-9640 (Injection) | Sumitomo Bakelite North America, Inc. | Phenolic | Sumikon® |
| CERTENE™ PHS-2 | Muehlstein | PP Homopolymer | CERTENE™ |
| Generic Phenolic - Glass Fiber | Generic | Phenolic | Generic |
| Hostacom TSOP EM5 2639 | LyondellBasell Industries | PP Copolymer | Hostacom |