RheTech Thermoplastic Polyolefin FT4702-00
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | RheTech, Inc. |
| Trademark: | RheTech Thermoplastic Polyolefin |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DwYvZm_RheTech-Thermoplastic-Polyolefin-FT4702-00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Thermoplasic Polyolefin, 190K Flexural Modulus, Non-UV Stabilized, Natural. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.978 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 17 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 66 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 19.3 | MPa | ASTM D638 |
| Flexural Modulus | 1310 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 400 | J/m | ASTM D256 |
| Dart Drop Impact | 20.3 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 110 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 51.1 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 - 82.2 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 199 - 227 | °C | |
| Middle Temperature | 204 - 232 | °C | |
| Front Temperature | 210 - 238 | °C | |
| Nozzle Temperature | 216 - 227 | °C | |
| Mold Temperature | 26.7 - 48.9 | °C | |
| Injection Pressure | 2.76 - 10.3 | MPa | |
| Holding Pressure | 2.07 - 8.27 | MPa | |
| Back Pressure | 0.345 - 1.03 | MPa |
| Injection instructions |
|---|
| Injection Speed: Variable -- Application DependantScrew RPM: Recovery 3 seconds before mold opensCycle Time: Wall Thickness Dependant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ J232WA | Prime Polymer Co., Ltd. | PP Random Copolymer | Prime Polypro™ |
| NILAMID® B3 D | Nilit Plastics | Nylon 6 | NILAMID® |
| Karina CLEAR PVC COMPOUND 80/201-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1-RG 3 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| POLYFORM C 2,5 | POLYMA Kunststoff GmbH & Co. KG | Acetal (POM) Homopolymer | POLYFORM |