Hostacom EKC 334N BLACK
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Dv3g1x_HostacomEKC334NBLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostacom EKC 334N BLACK is a 20% talc filled PP copolymer, with good stiffness, good toughness, low odour and low fogging. Product is available in black color, pellet form. This grade is not intended for medical, pharmaceutical, food and drinking water applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.04 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 17 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 25.0 | MPa | ISO 527-2 |
| Flexural Modulus 1(23°C) | 2400 | MPa | ISO 178/A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 95 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 65.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 150 | °C | ISO 306/A |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 128 HI FR | RTP Company | PP Copolymer | RTP |
| RTP PA66 50 GF BLK | RTP Company | Nylon 66 | RTP |
| TECHNO ABS 545L | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| Topolymer® 5711-901M | Dongguan Top Polymer Enterprise | TPE | Topolymer® |
| GAPEX® RPP30EB42BK | Ferro Corporation | PP, Unspecified | GAPEX® |