BESTNYL SE00VI01AT
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Triesa Plastics |
| Trademark: | BESTNYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DthhHy_BESTNYL-SE00VI01AT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6.6 natural lubrified and friction improved (PTFE), is perfect for final pieces that requires a minor wear out in final applications, also inertia to different chemical products and good resistance to humidity. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Water Absorption (23°C, 24 hr) | 0.90 | % | ISO 62 |
| Ash Content | 20 | % | Internal Method |
| Humidity - Pellets | 0.20 | % | ISO 1110 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 80 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2850 | MPa | ISO 527-2 |
| Tensile Stress | 81.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 15 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 230 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | > 235 | °C | ISO 306 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+18 | ohms | IEC 60093 |
| Electric Strength | 30 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 260 to 270 | °C | |
| Mold Temperature | 70.0 to 75.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| apilon 52bio® TB 65 | API SpA | TPU-Polyether | apilon 52bio® |
| Hifax CA 1110 G4 | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| Hifax TYC735P | LyondellBasell Industries | TPO (POE) | Hifax |
| Koylene ADL AS160NS | Reliance Industries Limited | PP Homopolymer | Koylene ADL |
| Kanghui KH2095 | Yingkou Kanghui Petrochemical Co., LTD. | PBT | Kanghui |