Rilsamid® AESN Noir P202 T6L
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | Arkema |
| Trademark: | Rilsamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DtDt22_Rilsamid-AESN-Noir-P202-T6L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsamid ® AESN Noir P202 T6L is a black coloured polyamide. This grade is plasticized and designed for tube extrusion. AESN Noir P202 T6L falls into the PA12-PHL category according to DIN 73378. MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Additive |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (235°C/5.0 kg) | 14.0 | cm³/10min | ISO 11357 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 61 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 440 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 28.0 | MPa | |
| Break | 49.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 25 | % | |
| Break | > 200 | % | |
| Flexural Modulus | 350 to 450 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | No Break | ||
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 172 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PA12-HIP, EHL, 22-004 | ISO 1874 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Melt Temperature | 260 to 280 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPRAN® WLFT 511BL | SAMBARK | TP, Unspecified | SUPRAN® |
| TOTAL Polystyrene rePS-8 | TOTAL Refining & Chemicals | PS (GPPS) | TOTAL Polystyrene |
| Nanjing Hongrui PA66 A306 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| 4MID® 9A22140 | 4Plas | Nylon 66 | 4MID® |
| Infino HM-1157 | LOTTE ADVANCED MATERIALS CO., LTD. | PC+ABS | Infino |