POLYFORT® FPP 40 GFC SHI
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | A. Schulman Europe |
| Trademark: | POLYFORT® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Dt6cne_POLYFORTFPP40GFCSHI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40% glass fiber reinforced high impact Homo Polypropylene |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 230°C/2.16 kg | 2.00 | cm³/10min | ISO 1133 |
| 230°C/5.0 kg | 7.00 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7700 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 78.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 5.5 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 6600 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| 4.5% strain | 120 | MPa | ISO 178 |
| 5.5% strain 3 | 112 | MPa | ISO 178 |
| 3.5% strain | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 8.0 | kJ/m² | ISO 179/1eA |
| 23°C | 14 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 55 | kJ/m² | ISO 179/1eU |
| 23°C | 60 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 154 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 147 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 163 | °C | ISO 306/A50 |
| -- | 120 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 39 | mm/min | ISO 3795 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Regrind | 20 | % | |
| Processing (Melt) Temp | 230 - 270 | °C | |
| Mold Temperature | 40 - 70 | °C |
| Injection instructions |
|---|
| *Drying normally not necessary. |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | at break |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren M1300R (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Copolymer | Sanren |
| Telcar® TL-1183A | Teknor Apex Company | TPE | Telcar® |
| VENELENE® 7700M | Poliolefinas Internacionales, C.A. (Polinter) | HDPE | VENELENE® |
| TRISTAR® PC-10R | Polymer Technology and Services, LLC | PC | TRISTAR® |
| LNP™ LUBRICOMP™ DX07035 compound | SABIC Innovative Plastics Europe | PC | LNP™ LUBRICOMP™ |