| Category: | PVC Homopolymer , Polyvinyl Chloride Homopolymer |
| Manufacturer: | Mexichem Specialty Resins, Inc. |
| Trademark: | Geon™ 210 Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DsX2Oz_Geon-210-Series-218.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Geon™210 Series 218 is a polyvinyl chloride homopolymer (PVC homopolymer) material,. The product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing methods are: slush molding, rotational molding, dip coating or coating. Geon™Typical application areas of 210 Series 218 are: additives/masterbatch |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Apparent Density 1 | 0.55 | g/cm³ | Internal method |
| K-Value 2 | 59.0 | Internal method | |
| Intrinsic Viscosity 3 | 0.74 | Internal method | |
| Particle Size 4 | Internal method | ||
| <105 mircron | 25.3 | % | Internal method |
| <125 mircron | 14.6 | % | Internal method |
| Average Particle Size 5 | 85 | µm | Internal method |
| Relative viscosity- Cyclohexanone 1% | 1.93 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze - fused 5 mins @ 350°F 6 | 53 | % | Internal method |
| Gloss- 60 degree fused 5 mins @ 350F 7 | 18 | % | Internal method |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brokfield Viscosity 8 | Internal method | ||
| Initial @ 2 rpm | 2.50 | Pa·s | Internal method |
| Initial @ 20 rpm | 2.45 | Pa·s | Internal method |
| One Day @ 2 rpm | 2.90 | Pa·s | Internal method |
| One Day @ 20 rpm | 2.73 | Pa·s | Internal method |
| Cut off the outflow- 95 psi 9 | 582.00 | g/10 min | Internal method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Vinyl Chloride Monomer 10 | ppm | Internal method | |
| Volatiles 11 | 0.050 | % | Internal method |
| polymerization process | Suspension | ||
| Gel temperature 12 | 88 | °C | Internal method |
| Test Method Formulas"ALTC" and "ASTM" Ingredients and Level Resin: 100 phr DINP: 57 phr ESO: 3 phr Therm-Chek SP 120 LOHF: 2 phr "STP" (all except Fog) Ingredients and Level Resin: 100 phr DOP: 60 phr "STP" (Fog only) Ingredients and Level Resin: 100 phr DUP: 80 phr |
| Note Message | |
|---|---|
| 1 . | STP 1169 |
| 2 . | 0.5g/100ml |
| 3 . | ASTM D 1243 60 A |
| 4 . | DFT 1466 |
| 5 . | DFT 1466 |
| 6 . | ATLC 66 |
| 7 . | ALTC 65 |
| 8 . | ALTC 22 |
| 9 . | ALTC 23 |
| 10 . | STP 1005 |
| 11 . | STP 1242 |
| 12 . | ATLC 29 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 602 | RTP Company | ABS | RTP |
| Ferro PP TPP21AN89HB NATURAL | Ferro Corporation | PP Homopolymer | Ferro PP |
| ESPRENE EPDM 532 | Sumitomo Chemical Co., Ltd. | EPDM | ESPRENE EPDM |
| Iupilon® ECF2010R | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| Plaslube® PA6 TL10 | Techmer Engineered Solutions | Nylon 6 | Plaslube® |