Pearlbond™ 12F75UV is a UV-resistant standard polyester-based TPU supplied in form of translucent, colourless pellets, featuring a low melting point and very low gel content. Processed by extrusion and compounding. APPLICATIONS Pearlbond™ 12F75UV is designed for a wide variety of adhesive film applications requiring excellent adhesion in combination with good heat resistance and dry cleaning resistance. This grade can be both cast extruded and blown. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- 1 | 1.15 | g/cm³ | ASTM D792 |
| 20°C | 1.15 | g/cm³ | ISO 2781 |
| Melt Mass-Flow Rate (MFR) (190°C/10.0 kg) | 40 - 65 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 78 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| -- | 30.0 | MPa | ISO 527-2 |
| 100% strain | 4.00 | MPa | ISO 527-2 |
| 300% strain | 7.00 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 530 | % | ISO 527-2 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 4.00 | MPa | ASTM D412 |
| 300% strain | 7.00 | MPa | ASTM D412 |
| Tensile Strength | 30.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 530 | % | ASTM D412 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 130 - 140 | °C | Internal method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Softening Range | 110 - 130 | °C | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Extruder Screw L/D Ratio | 25.0:1.0 to 30.0:1.0 | ||
| Extruder Screw Compression Ratio | 2.0:1.0 to 3.0:1.0 | ||
| Drying Temperature | 90 - 105 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Cylinder Zone 1 Temp. | 145 - 155 | °C | |
| Cylinder Zone 2 Temp. | 155 - 165 | °C | |
| Cylinder Zone 3 Temp. | 165 - 170 | °C | |
| Cylinder Zone 4 Temp. | 170 - 180 | °C | |
| Die Temperature | 170 - 180 | °C |
| Note Message | |
|---|---|
| 1 . | 20°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6 7500 GF 15 H | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| WACKER SilGel® 613 A/B | Wacker Chemie AG | Silicone | WACKER SilGel® |
| HiFill® PA6 GF25 L BK | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| LNP™ COLORCOMP™ 144C compound | SABIC Innovative Plastics | PC | LNP™ COLORCOMP™ |
| Monprene® RG-17260 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |