ACCUTECH™ HP0334W20L
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUTECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DqoyLD_ACCUTECH-HP0334W20L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUTECH™HP0334W20L is a polypropylene homopolymer (PP Homopoly) product containing 20% wollastonite (casio3). It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 34.0 | MPa | ASTM D638 |
| Fracture | 28.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 6.0 | % | ASTM D638 |
| Fracture | 16 | % | ASTM D638 |
| Flexural Modulus | 2300 | MPa | ASTM D790 |
| Flexural Strength | 42.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 42 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 115 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 65.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Ash Content, ASTM D2584: 20% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MarFlex® 7105D | Chevron Phillips Chemical Company LLC | LLDPE | MarFlex® |
| TOTAL Polystyrene FT 878 | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |
| LNP™ THERMOCOMP™ QF007 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ THERMOCOMP™ |
| OP - ABS ABS 4-8 SS | Oxford Polymers | ABS | OP - ABS |
| Sylvin 9604-90 White 190 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |