Plexiglas® Resist zk4HC

Category:	Acrylic (PMMA) , Polymethyl Methacrylate Acrylic
Manufacturer:	Evonik Industries AG
Trademark:	Plexiglas®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Dq86ke_Plexiglas-Resist-zk4HC.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Product Profile:
PLEXIGLAS® Resist zk4HC is an amorphous, impact-modified thermoplastic molding compound (PMMA-I).

Typical properties of impact-modified PLEXIGLAS® molding compounds are

high weather resistance

excellent transmission and clarity

brilliant appearance

the pleasant feel and sound of the moldings.

PLEXIGLAS® Resist zk4HC is characterized by the
following special properties:

improved break resistance and impact strength

best resistance to stress cracking of all impact-modified PLEXIGLAS molding compounds

AMECA listing.

Application:
Used for extruding and coextruding sheets and profiles.

Examples:
extruded/coextruded sheets and profiles for automotive bodies and the sanitaryware sector (bathtubs and shower trays) or crystal-clear luminare covers for industrial plants that come into contact with aggressive media.

General Information
Additive	Impact Modifier
Features	Good Weather Resistance High Clarity High ESCR (Stress Crack Resist.) High Impact Resistance Pleasing Surface Appearance
Uses	Automotive Applications Automotive Bumper Automotive Exterior Parts Automotive Exterior Trim Profiles Protective Coverings Sanitary Products Sheet
Forms	Pellets
Processing Method	Coextrusion Extrusion
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Nominal Value	Unit	Test Method
Density	1.18	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (230°C/3.8 kg)	1.10	cm³/10min	ISO 1133
Water Absorption			ISO 62
23°C, 24 hr	2.0	%
Equilibrium, 23°C, 50% RH	0.60	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2900	MPa	ISO 527-2/1
Tensile Stress (Yield)	68.0	MPa	ISO 527-2/50
Tensile Strain (Yield)	4.5	%	ISO 527-2/50
Nominal Tensile Strain at Break	17	%	ISO 527-2

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	25	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Glass Transition Temperature	108	°C	ISO 11357-2
Vicat Softening Temperature	102	°C	ISO 306/B50
CLTE - Flow (0 to 50°C)	8.0E-5	cm/cm/°C	ISO 11359-2

Flammability	Nominal Value		Test Method
Flame Rating (1.60 mm)	HB		UL 94
Fire Rating	B2		DIN 4102

Optical	Nominal Value	Unit	Test Method
Refractive Index	1.490		ISO 489
Transmittance ¹	92.0	%	ISO 13468-2

Extrusion	Nominal Value	Unit
Drying Temperature	< 90.0	°C
Drying Time	2.0 to 3.0	hr
Melt Temperature	220 to 260	°C
Die Temperature	220 to 260	°C

Note Message
1 .	D65

Resin Grade	Manufacturer	Category	Trademark
Quantum Composites QC-3100	Quantum Composites Inc.	Vinyl Ester	Quantum Composites
Monprene® OM-10275-01	Teknor Apex Company	TPE	Monprene®
BLUESTAR® POM BS025	Shanghai BlueStar New Chemical Materials Co., Ltd.	Acetal (POM) Copolymer	BLUESTAR® POM
GETILAN GPE/134	Crosspolimeri S.p.A.	XLPE	GETILAN
ICORENE® 9105 V0 Grey 7005	ICO Polymers EMEA, A Division of A. Schulman	LLDPE	ICORENE®