Bakelite® PF 6507
| Category: | Phenolic , Phenolic |
| Manufacturer: | Hexion Inc. |
| Trademark: | Bakelite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DoqAmX_Bakelite-PF-6507.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product Description Phenolic moulding compound, inorganically filled, glass fibre reinforced, elastomer modified, galvanizable, heat-resistant, good media resistance, high dimensional stability at raised temperature, high mechanical strength Application Areas Cooling pumps, solenoid switch covers, magnetic switches, mechanically and thermally highly stressed parts in automotive construction, electrical motor end shields, housing parts, pulleys, tension return pulleys, cog wheels, impellers, bearing parts |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.60 | g/cm³ | ISO 1183 |
| Apparent Density | 0.72 | g/cm³ | ISO 60 |
| Molding Shrinkage 1 | 0.20 | % | ISO 2577 |
| Water Absorption - 24h/23C | 15.0 | mg | ISO 62 |
| Post Shrinkage 2 | 0.15 | % | ISO 2577 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | > 15.0 | MPa | |
| Compression Molding Temperature | 160 to 190 | °C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 250 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10500 | MPa | ISO 527-2/1 |
| Tensile Stress | 85.0 | MPa | ISO 527-2/5 |
| Flexural Modulus | 10000 | MPa | ISO 178 |
| Flexural Stress 3 | 135 | MPa | ISO 178 |
| Compressive Stress | 250 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 15 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (8.0 MPa, Unannealed) | 170 | °C | ISO 75-2/C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength 4(1.00 mm) | 23 | kV/mm | IEC 60243-1 |
| Relative Permittivity (100 Hz) | 7.00 | IEC 60250 | |
| Dissipation Factor (100 Hz) | 0.10 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 150 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 60.0 to 75.0 | °C | |
| Nozzle Temperature | 80.0 to 100 | °C | |
| Processing (Melt) Temp | 80.0 to 100 | °C | |
| Mold Temperature | 160 to 190 | °C | |
| Injection Pressure | > 15.0 | MPa | |
| Back Pressure | 0.500 to 2.00 | MPa |
| Note Message | |
|---|---|
| 1 . | Injection |
| 2 . | Injection |
| 3 . | 2.0 mm/min |
| 4 . | short term, electrode layout P25mm/P25mm in transformer oil equivalent to IEC 60296 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 207 MS | RTP Company | Nylon 66 | RTP |
| TEKAMID™ TA250G60 | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| BP RPPC 2008 C BLK | Buckeye Polymers, Inc. | PP Copolymer | BP |
| EL-Lene™ D682PC | SCG Chemicals Co., Ltd. | LLDPE | EL-Lene™ |
| KEBAFORM® C 6027 | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |