LNP™ THERMOCOMP™ SF008 compound
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DoXGGx_LNP-THERMOCOMP-SF008-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP SF008 is a compound based on Nylon 12 resin containing 40% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound SF-1008 Product reorder name: SF008 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 | % | ASTM D955 |
| Across Flow : 24 hr | 0.70 | % | ASTM D955 |
| Across Flow : 24 hr | 0.73 | % | ISO 294-4 |
| Flow : 24 hr | 0.18 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8270 | MPa | ASTM D638 |
| -- | 8760 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 136 | MPa | ASTM D638 |
| Break | 152 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 11 | % | ASTM D638 |
| Break | 9.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 7580 | MPa | ASTM D790 |
| -- | 9000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 96.5 | MPa | ASTM D790 |
| -- | 213 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 260 | J/m | ASTM D256 |
| 23°C 2 | 18 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1400 | J/m | ASTM D4812 |
| 23°C 3 | 76 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 177 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 170 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 166 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 216 to 227 | °C | |
| Middle Temperature | 221 to 232 | °C | |
| Front Temperature | 227 to 238 | °C | |
| Processing (Melt) Temp | 227 to 238 | °C | |
| Mold Temperature | 71.1 to 82.2 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRIPRO K1108 | Formosa Plastics Corporation | PP Homopolymer | TAIRIPRO |
| Titalon® 1300GFT | Titan Plastics Compounds Co., Ltd. | Nylon 6 | Titalon® |
| ASTAGLAS™ DR101 | Marplex Australia Pty. Ltd. | Acrylic (PMMA) | ASTAGLAS™ |
| PLUSTEK PB300G33/310G6 | Polyram Ram-On Industries | Nylon 6 | PLUSTEK |
| Sylvin 9077-65 Grey 9507 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |