KOCETAL® WR301LOBK
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Kolon Plastics, Inc. |
| Trademark: | KOCETAL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Dncc2Y_KOCETAL-WR301LOBK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KOCETAL® WR301LOBK is an Acetal (POM) Copolymer product. It is available in Asia Pacific, Europe, Latin America, or North America. Typical application: Automotive. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 11 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 2.0 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 0.22 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 80 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 57.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 55 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2300 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 84.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 63 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648A | ||
| 0.45 MPa, Unannealed | 158 | °C | |
| 1.8 MPa, Unannealed | 110 | °C | |
| Melting Temperature | 166 | °C | ASTM D1525 |
| CLTE - Flow | 1.3E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+11 | ohms·cm | ASTM D257 |
| Dielectric Strength | 19 | kV/mm | ASTM D149 |
| Dielectric Constant | 3.70 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.060 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2205 TFE 10 | RTP Company | PEEK | RTP |
| RenPIM® VG 5234 Polyol/ 5234 Isocyanate | Huntsman Advanced Materials | PUR, Unspecified | RenPIM® |
| MIDILENA III PPF400BO2 | ROMPETROL PETROCHEMICALS S.R.L. | PP Homopolymer | MIDILENA III |
| Moplen HP462R | LyondellBasell Industries | PP Homopolymer | Moplen |
| POLYFLAM® RPP 500 D | A. Schulman Europe | PP Homopolymer | POLYFLAM® |