THERMOLAST® K TC8LEZ (Series: UV/FG)
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | KRAIBURG TPE |
| Trademark: | THERMOLAST® K |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DnXONB_THERMOLAST-K-TC8LEZ-Series-UV-FG-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The UV/FG Series is your material solution for applications requiring high UV resistance. It is particularly appropriate for automotive exterior and interior components. Typical applications
Material advantages
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.980 | g/cm³ | ISO 1183 |
| Spiral Flow 1 | 58.0 | cm |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 80 | ISO 7619 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 2(Yield) | 11.0 | MPa | ISO 37 |
| Tensile Elongation 3(Break) | 750 | % | ISO 37 |
| Tear Strength 4 | 28 | kN/m | ISO 34-1 |
| Compression Set 5 | ISO 815 | ||
| 23°C, 72 hr | 34 | % | |
| 70°C, 24 hr | 55 | % | |
| 100°C, 24 hr | 78 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 to 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 180 | °C | |
| Middle Temperature | 200 | °C | |
| Front Temperature | 220 | °C | |
| Mold Temperature | 25.0 to 40.0 | °C | |
| Injection Pressure | 20.0 to 100 | MPa | |
| Back Pressure | 2.00 to 10.0 | MPa |
| Note Message | |
|---|---|
| 1 . | Injection Pressure: 70.0 bar |
| 2 . | Type S2, 200 mm/min |
| 3 . | Type S2, 200 mm/min |
| 4 . | Method Bb, Angle (Nicked) |
| 5 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| EMOPLEN® CP-R 47.70 | EMAS Plastik San.Tic.AS. | PP Copolymer | EMOPLEN® |
| Hanwha Total PP B230D | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, HMS | Hanwha Total PP |
| Innothane® FM-109 | Innovative Polymers, Inc. | TSU | Innothane® |
| 3M™ Dyneon™ Perfluoroelastomer PFE 7104BZ | 3M Advanced Materials Division | Perfluoroelastomer | 3M™ Dyneon™ Perfluoroelastomer |
| LEXAN™ LUX7189 resin | SABIC Innovative Plastics | PC | LEXAN™ |