| Star T PA6 75E12 is a Polyamide 6 Injection Molding Resin with Improved Thermal Conductivity |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.26 | g/cm³ | ASTM D792 |
| shrinkage- Flow (4.00 mm) | 0.80 - 1.2 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 85.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.4 | % | ISO 527-2 |
| Flexural Modulus | 12500 | MPa | ISO 178 |
| Flexural Stress | 123 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 3.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 20 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1(1.8 MPa, Unannealed, 64.0 mm Span) | 136 | °C | ISO 75-2/Af |
| Thermal Conductivity 2 | 1.5 | W/m/K | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 250 - 260 | °C | |
| Middle Temperature | 260 - 280 | °C | |
| Front Temperature | 260 - 280 | °C | |
| Processing (Melt) Temp | 260 - 280 | °C | |
| Mold Temperature | 60 - 90 | °C |
| Note Message | |
|---|---|
| 1 . | 80x10x4 mm |
| 2 . | Across Flow |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Daelim Po1y® PP-333J | DAELIM INDUSTRIAL CO., LTD. | PP Random Copolymer | Daelim Po1y® |
| FHR Polypropylene AP5206-HN | Flint Hills Resources, LP | PP Impact Copolymer | FHR Polypropylene |
| Latilub 88/50-30GRT | LATI S.p.A. | PEEK | Latilub |
| LNP™ THERMOCOMP™ HB006 compound | SABIC Innovative Plastics | Nylon 11 | LNP™ THERMOCOMP™ |
| LNP™ LUBRICOMP™ Lexan_LF1520A compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |