AKROMID® A3 GF 30 4 natural (3396)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Dn89de_AKROMID-A3-GF-30-4-natural-3396-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A3 GF 30 4 natural (3396) is a 30% glass fibre reinforced, high heat stabilised, hydrolysis- and chemical resistant polyamide 6.6 with characteristic colour. Applications are functional parts in the heating- and cooling system in the automotive industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.36 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 76.0 | -- | cm | Internal Method |
| Water Absorption (Saturation, 23°C) | 4.5 | -- | % | ISO 62 |
| Humidity Absorption - 62% RH (70°C) | 1.9 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flexural Strain at Break 1 | 4.0 | -- | % | ISO 178 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 30 | -- | % | ISO 1172 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10000 | 6700 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 200 | 130 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.7 | 7.0 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 9500 | -- | MPa | ISO 178 |
| Flexural Stress 3 | 300 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 10 | -- | kJ/m² | |
| 23°C | 12 | 17 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -40°C | 73 | -- | kJ/m² | |
| 23°C | 100 | 100 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 253 | -- | °C | ISO 75-2/A |
| Melting Temperature 4 | 262 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10 K/min, DSC |
| 5 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 7051SS | Resinoid Engineering Corporation | Phenolic | Resinoid |
| Monprene® CP-23144 | Teknor Apex Company | TPE | Monprene® |
| Taitacell EPS-361ML | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| Daelim Po1y® XP3300EN | DAELIM INDUSTRIAL CO., LTD. | mLLDPE | Daelim Po1y® |
| Sylvin 9067-90LMW Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |