Synres-Almoco AMC 2567
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Synres-Almoco BV |
| Trademark: | Synres-Almoco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DmMTGX_Synres-Almoco-AMC-2567.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Glass-fibre reinforced Polyester moulding compound Outstanding mechanical strength similar to BMC/SMC, very good electrical isolation properties and dimensional stability, excellent processability Primary application(s): Connectors, Bobbins, Housings, Mounting plates This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.00 to 2.20 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 to 0.85 | g/cm³ | ISO 60 |
| Molding Shrinkage - Flow 1 | 0.15 to 0.45 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | < 0.30 | % | ISO 62 |
| Post Shrinkage 2 | < 0.050 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2 | ||
| Compression Molded | 6000 to 9000 | MPa | |
| Injection Molded | 13000 to 15000 | MPa | |
| Tensile Stress | ISO 527-2 | ||
| Compression Molded | 35.0 to 60.0 | MPa | |
| Injection Molded | 60.0 to 70.0 | MPa | |
| Flexural Modulus | ISO 178 | ||
| Compression Molded | 8000 to 12000 | MPa | |
| Injection Molded | 8000 to 12000 | MPa | |
| Flexural Stress | ISO 178 | ||
| Compression Molded | 80.0 to 100 | MPa | |
| Injection Molded | 120 to 140 | MPa | |
| Compressive Stress | 120 to 170 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| Compression Molded | 2.5 to 3.5 | kJ/m² | |
| Injection Molded | 3.5 to 5.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| Compression Molded | 5.0 to 10 | kJ/m² | |
| Injection Molded | 9.0 to 14 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | > 200 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 100 to 120 | °C | ISO 75-2/C |
| CLTE - Flow (50 to 100°C) | 1.0E-5 to 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.90 to 1.1 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 to 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 to 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 25 to 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 6.00 5.00 | ||
| 1 MHz | 5.00 4.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.010 to 0.030 | ||
| 1 MHz | 0.010 to 0.030 | ||
| Arc Resistance | PLC 4 | ASTM D495 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.600 mm | V-1 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 930 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | Compression Molded |
| 2 . | 168 h / 110°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Cheng Yu NG1200S | Cheng Yu Plastic Company Limited | Nylon 66 | Cheng Yu |
| Durethan® BKV 215 H2.0 DUS035 900051 | LANXESS GmbH | Nylon 6 | Durethan® |
| Laticonther 47/1 CP/80 | LATI S.p.A. | PP Copolymer | Laticonther |
| Karina GRAY COLOR CONCENTRATE 18/15-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Piolen® P KEMLA105 | PiO Kunststoffe GmbH & Co KG | PP+EPDM | Piolen® P |