LNP™ LUBRICOMP™ KFL36 compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DkMmYd_LNPLUBRICOMPKFL36compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP KFL36 is a compound based on Acetal Copolymer resin containing Glass Fiber, PTFE. Also known as: LNP* LUBRICOMP* Compound KFL-4036 Product reorder name: KFL36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.72 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.30 - 0.50 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 117 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.3 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 7100 | MPa | ISO 178 |
| Flexural Stress | 123 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 3(23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 20 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5(1.8 MPa, Unannealed, 64.0 mm Span) | 157 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 - 188 | °C | |
| Middle Temperature | 193 - 204 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Processing (Melt) Temp | 199 - 216 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8946-80 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NEXT REPROCESSED ABS 342-300RG | NEXT Specialty Resins, Inc. | ABS | NEXT REPROCESSED |
| Fainplast PVC FKA 0753 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| KEBAPEAK® PEEK XC1730 | BARLOG plastics GmbH | PEEK | KEBAPEAK® |
| Karina WHITE PVC COMPOUND -E 838-10/182-Y-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |