IROGRAN® CA116-201
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Huntsman Corporation |
| Trademark: | IROGRAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DiUNqb_IROGRAN-CA116-201.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
IROGRAN CA116-201 is a high performance polyester based thermoplastic polyurethane intended for flat die extrusion applications. IROGRAN CA116-201 is part of the HUNTSMAN film and sheet product range and offers a specially designed, flexible plasticizer free product suitable for the preparation of extruded films. PERFORMANCE FEATURES
APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.15 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 15 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| Shore A, Injection Molded | 95 | ASTM D2240 | |
| Injection Molded | 95 | DIN 53505 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 2 | ASTM D412 | ||
| 100% Strain, 0.635 mm | 6.07 | MPa | |
| 300% Strain, 0.635 mm | 6.86 | MPa | |
| Tensile Strength 3 | |||
| Break, 0.635 mm | 24.8 | MPa | ASTM D412 |
| Break, 0.635 mm | 33.0 | MPa | DIN 53504 |
| Tensile Elongation 4 | |||
| Break, 0.635 mm | 600 | % | ASTM D412 |
| Break, 0.635 mm | 400 | % | DIN 53504 |
| Tear Strength 5 | |||
| 0.635 mm | 92.8 | kN/m | ASTM D624 |
| 6.35 mm | 75 | kN/m | DIN 53515 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 80.0 to 150 | °C | |
| TMA 6(635.0 µm) | 90 to 120 | °C | Internal Method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 4.44 | °C | |
| Drying Time | 4.0 | hr | |
| Hopper Temperature | 160 | °C | |
| Cylinder Zone 1 Temp. | 170 | °C | |
| Cylinder Zone 2 Temp. | 170 | °C | |
| Cylinder Zone 3 Temp. | 170 | °C | |
| Cylinder Zone 4 Temp. | 170 | °C | |
| Cylinder Zone 5 Temp. | 170 | °C | |
| Adapter Temperature | 170 | °C | |
| Die Temperature | 170 | °C |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | Extruded Film |
| 3 . | Extruded Film |
| 4 . | Extruded Film |
| 5 . | Extruded Film |
| 6 . | Extruded Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 陶氏低密度聚乙烯 113C | The Dow Chemical Company | LDPE | DOW™ LDPE |
| NEXUS PC PC701 | Nexus Resin Group, LLC. | PC | NEXUS PC |
| Adell Polyamide AW-18 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| Alpha PVC 3019-40/45 CLEAR 0003 | AlphaGary | PVC, Flexible | Alpha PVC |
| Gallonprene® GP520-6504 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |